On the quantification of the constraint effect along a three-dimensional crack front
In this paper we examined the characterization of constraint effects for surface cracked plates under uniaxial and biaxial tension loadings. First, three-dimensional (3D) modified boundary layer analyses were conducted using the finite element method to study the constraint effect at a typical 3D crack front. The analyses were carried out using small geometry change formulation and deformation plasticity material model. Elastic-plastic crack front stress fields at a constant J and various T-stress levels were obtained. Three-dimensional elastic-plastic analyses were performed for semi-circular surface cracks in a finite thickness plate, under remote uniaxial and biaxial tension loading conditions. In topological planes perpendicular to the crack fronts, the crack stress fields were obtained. Then, J-Q and J-T two-parameter approaches are used in characterizing the elastic-plastic crack-tip stress fields along the 3D crack front. It is found that the J-Q characterization provides good estimate for the constraint effect for crack-tip stress fields. Reasonable agreements are achieved between the T-stress based Q-factors and the Q-factors obtained from finite element analysis. Copyright
|Keywords||Biaxial loading, Constraint effects, Elastic-plastic fracture mechanics, Q-factors, Surface cracked plate, T-stress|
|Conference||36th ASTM National Symposium on Fatigue and Fracture Mechanics|
Wang, X. (2009). On the quantification of the constraint effect along a three-dimensional crack front. In ASTM Special Technical Publication (pp. 87–102).